Accelerated deactivation studies of the natural-gas oxidation catalyst-Verifying the role of sulfur and elevated temperature in catalyst aging
Honkanen,Mari; Kärkkäinen,Marja; Kolli,Tanja; Heikkinen,Olli; Viitanen,Ville; Zeng,Lunjie; Jiang,Hua; Kallinen,Kauko; Huuhtanen,Mika; Keiski,Riitta L.; Lahtinen,Jouko; Olsson,Eva; Vippola,Minnamari (2016)
This publication is copyrighted. You may download, display and print it for Your own personal use. Commercial use is prohibited
Julkaisun pysyvä osoite on
Accelerated deactivation, caused by thermal aging (TA) and/or sulfur+water poisoning (SW), of the PtPd/γ-Al2O3 natural-gas oxidation catalyst was studied. Thermal aging and poisoning treatments were performed separately and with varied combinations and comprehensive characterization of the catalyst was carried out after each step. The fresh catalyst has small, oxidized PtPd particles (<5nm) uniformly distributed in the γ-alumina washcoat. After the SW-treatment, a small amount of bulk aluminum sulfate was observed near the slightly grown noble metal particles. During the thermal aging, γ-alumina changed to δ-/θ- and α-alumina. In addition, total decomposition of oxidized Pt and partly decomposition of oxidized Pd occurred resulting in the formation of the grown noble metal particles with a bimetallic PtPd core and a polycrystalline PdO shell. Also few, small (~5nm) bimetallic PtPd particles were still detected. In the TA+SW-treated catalyst with grown noble metal particles, a small amount of bulk aluminum sulfate was detected and it was randomly distributed over the noble metal particles and washcoat. The activity in the terms of methane conversion over the TA-, SW-, and SW+TA-treated catalysts was similar but it was decreased compared to the fresh catalyst. The activity of the TA+SW-treated catalyst was drastically decreased compared to the fresh catalyst due to significant morphological changes and aluminum sulfate formation.
- TUNICRIS-julkaisut 
Näytetään aineisto, joilla on samankaltaisia nimekkeitä, tekijöitä tai asiasanoja.
Maggioni,Matteo; Sanchez-Monge,Enrique; Foi,Alessandro (2014)
Supramolecular hierarchy among halogen and hydrogen bond donors in light-induced surface patterning Saccone,Marco; Dichiarante,Valentina; Forni,Alessandra; Goulet-Hanssens,Alexis; Cavallo,Gabriella; Vapaavuori,Jaana; Terraneo,Giancarlo; Barrett,Christopher J.; Resnati,Giuseppe; Metrangolo,Pierangelo; Priimägi,Arri (28.01.2015)
/dk/atira/pure/researchoutput/researchoutputtypes/contributiontojournal/articleHalogen bonding, a noncovalent interaction possessing several unique features compared to the more familiar hydrogen bonding, is emerging as a powerful tool in functional materials design. Herein, we unambiguously show ...
Virkki,Matti; Tuominen,Ossi; Forni,Alessandra; Saccone,Marco; Metrangolo,Pierangelo; Resnati,Giuseppe; Kauranen,Martti; Priimägi,Arri (2015)
/dk/atira/pure/researchoutput/researchoutputtypes/contributiontojournal/articleWe demonstrate that halogen bonding strongly enhances the nonlinear optical response of poled supramolecular polymer systems. We compare three nonlinear optical chromophores with similar electronic structures but different ...